NIST Highlights Leite’s “Battery Perimortems"

Research published by Department of Materials Science and Engineering (MSE) and Institute for Research in Applied Physics (IREAP) professor Marina Leite, MSE adjunct professor Alec Talin (Sandia National Labs) and their colleagues–the first to describe a way to observe solid state batteries as they fail–was highlighted in the National Institute of Standards and Technology’s Tech Beat.

The procedure, which has previously been featured in Clark School news, uses a combination of imaging techniques to watch solid-state lithium-ion batteries in realtime as they charge and discharge. In the published study, Leite and her team used it to discover why aluminum anodes, which could help make batteries lighter and cheaper, degrade so quickly. The problem was traced to the formation of “mounds” on the surface of the aluminum. These structures both permanently trapped lithium and blocked still-free lithium ions from participating in the charge/discharge cycle. An additional barrier was created when the naturally occurring aluminum oxide on the anode’s surface reacted with lithium to form a stable alloy that surrounded the mounds.

In the piece by Mark Esser, Leite describes the typical method of studying before and after microscopy “snapshots” of batteries, which are used to infer how failure occurs, as “postmortems.”

“[But] in our case,” she adds, “we could follow as the morphology changed on the anode’s surface and track how it impacted the performance of the battery, quantifying the capacity loss while charging and discharging the battery and mimicking what happens when a battery is in use.”

Read the full Tech Beat article:

“New Imaging Technique Finds Formation of Aluminum Alloys to Blame for Next-Gen Battery Failures”

March 10, 2015


Prev   Next

Current Headlines

Protection Collections Abound for Local Health Care Workers

Researchers from Poland report results aided by UMD's AIM Lab

Slam Dunk at Alumni Cup

Clark School Graduate Engineering Program Ranked 20th Nationally

Robert Briber Named Interim Dean of Clark School

2020 Hulka/Wells Energy Fellowships Awarded

Hafezi, Antonsen, Sprangle receive 2020 MURI Awards

Dean Pines Named University of Maryland's 34th President

News Resources

Return to Newsroom

Search News

Archived News

Events Resources

Events Calendar

Additional Resources

UM Newsdesk

Faculty Experts